Anti-tack powder compound release agent composes of fine inorganic fillers, active substances and tensides. The product shows the excellent dispersion stability in water and excellent wetting of the rubber sheets. Even if at low dispersion concentration, there is no separation and sediment within several hours. Thus it is very positive to avoid forming dispersion slurry at the bottom of dipping tank. The product forms a thin, flexible film on the surface of milled sheets, consequently there is a very good release effect. There is sufficient friction to prevent the sheets from slipping during storage and to allow smooth, continuous feeding of the extruders. Furthermore the film is non-dusty and the built-up on the equipment is minimized. Anti-tack powder compound release agent can fast drying on the slabs, it has low foam performance、no negative effects on health and environment and no dusting etc.

The application concentration is recommended at 3.0±1%, depending on type of rubber compound, environment temperature. For best performance we recommended to use a separate dispersion tank that is equipped with a paddle stirrer. The powder is added to the warm water, ideally around 60℃. The dispersion should be stirred for at least 30min before use. Especially if cold water is used the dispersion time should be extended as long as possible. During the batch off process only slight agitation is needed to prevent sedimentation. Usually the motion of the bath due to the dipping process is already enough. It is very necessary to add / feed the fresh dispersion into the dipping tank in time. The liquid level of dispersion in dipping tank should keep up to 2/3 volume.

Used for mixing process of Tire, Hose and Rubber products manufacturing, to prevent the sticking together of uncured rubber and milled sheet.

*

Anti-tack powder compound release agent composes of fine inorganic fillers, active substances and tensides. The product shows the excellent dispersion stability in water and excellent wetting of the rubber sheets. Even if at low dispersion concentration, there is no separation and sediment within several hours. Thus it is very positive to avoid forming dispersion slurry at the bottom of dipping tank. The product forms a thin, flexible film on the surface of milled sheets, consequently there is a very good release effect. There is sufficient friction to prevent the sheets from slipping during storage and to allow smooth, continuous feeding of the extruders. Furthermore the film is non-dusty and the built-up on the equipment is minimized. Anti-tack powder compound release agent can fast drying on the slabs, it has low foam performance、no negative effects on health and environment and no dusting etc.

The application concentration is recommended at 3.0±1%, depending on type of rubber compound, environment temperature. For best performance we recommended to use a separate dispersion tank that is equipped with a paddle stirrer. The powder is added to the warm water, ideally around 60℃. The dispersion should be stirred for at least 30min before use. Especially if cold water is used the dispersion time should be extended as long as possible. During the batch off process only slight agitation is needed to prevent sedimentation. Usually the motion of the bath due to the dipping process is already enough. It is very necessary to add / feed the fresh dispersion into the dipping tank in time. The liquid level of dispersion in dipping tank should keep up to 2/3 volume.

Used for mixing process of Tire, Hose and Rubber products manufacturing, to prevent the sticking together of uncured rubber and milled sheet.